MARBLE AND NATURAL STONE ADHESIVE
- Rapid cure time (3-5 min. at 25ºC).
- Very low shrinkage during hardening.
- Easy to apply
- Excellent brightness after the use of grinding machines.
- Superior resistance to wear of time
- High reactivity
- Chemically inert and offers extended durability
- Very good adhesion on natural stones even at higher temperatures
- Temperature resistance of cured adhesive is between 10oC and +100oC
- Bonded surfaces are ready to use after 2 hours
- No color change, cracking or shrinkage during hardening period
- The surface must be clean and free from dust and grease.
- A component is mixed with b component / hardener at the rate of %2-3 until a homogenous mixture is obtained then applied on the surface.
- A homogeneous mixing facilitates uniform catalysis.
- The hardener rate depends on temperature and the quantity of the component.
- An excess of hardener increase the hardening speed but weakens the adhesive seal.
- The surface to be treated must be clean and dry, porosity and the roughness of the surface, favor best adhesion.
- Spatula
|
PRODUCT |
VOLUME |
PACKAGE |
|
MARBLE & STONE ADHESIVE |
1200 gr |
12 |
|
MARBLE & STONE ADHESIVE |
2500 gr |
6 |
|
MARBLE & STONE ADHESIVE |
5 kg |
4 |
|
MARBLE & STONE ADHESIVE |
30 kg |
1 |
- Uncured product can be removed with a suitable solvent.
- Mixing the components in correct ratio is critical since the amount of hardener affect working time.
- In wall covering application or in case of high range of temperature changes use fixed pins or suitable supports.
- The color of the hardened adhesive may change color in case of ultraviolet light exposure.
- Keep the container tightly closed during the application.
- Apply the resin on a dry and clean surface.
- Hardened adhesive is workable after 2-6 hours.
- Irritating to eyes and skin. Avoid contacting eyes
- Do not inhale.
- If eyes contact occurs, immediately flush eyes with plenty of water and consult a doctor.
- Use only in well-ventilated areas.
- Keep away from fire.
- Keep locked up and away from children.
- Wear gloves during application.
|
Color |
Beige (Comp A) White (Comp B) |
|
Consistency |
:Tixotrophic |
|
Density |
1,85 ± 0,02 gr/cm3 (+20˚C /Comp.A); 1.8085 gr/cm3 (+20˚C /Comp.B) |
|
Viscosity |
:25˚C 20rpm 200000-350000cps |
|
Type |
Solvent based / Contains styrene/ Polyester based |
|
Mix ratio |
: %2-3 BPO |
|
Working time |
: 5-10 min. |
|
Application temperature |
: +5˚C to +40˚C |
|
Mixing time |
: ~ 1min. |
|
Min Cure time |
: ~3.5 - 5 min. |
|
Full Cure time |
: 10-12 min. |
|
Flash Point |
:33˚C (Comp A) :50˚C (CompB) |
|
Max. Exotherm during reaction |
: 110 - 115˚C |
|
Min working temperature |
: 5˚C |
|
Max heat resistance |
: 100˚C |
|
Maximum force (kgf) |
: 490 |
|
Maximum elongation (∆/mm) |
:1.18 |
|
Maximum traction (kg /mm2) |
:3.8 |
|
Traction force (kgf) |
:490 |
|
Elongation (∆/mm) |
:1.29 |
|
Elongation % |
: 1.7 |